AA-Bond 201 50 ML Industrial Strength, Fast Cure Epoxy, Quick Dry, Two Minute Epoxy 2 Hour Cure Time 50ML

PRODUCT DESCRIPTION AA-BOND 201 is an exceptional epoxy formulation recommended for lower temperature or wet industrial grade bonding applications where FAST CURING is required. AA-BOND 201 is versatile two-part epoxy system contains no solvents, mixes easily at room temperature, and is suitable for high performance structural bonding applications where the combination of very fast room temperature curing coupled with low shrinkage and excellent mechanical and electrical properties is needed. AA-BOND 201 develops strong, tough bonds to metals, plastics, concrete, sheetrock, marble, stone, rock, tile, plaster, cement, glass and glass fabrics, hardboards and forestry products, ceramics, rubber, masonry materials, and other construction materials. AA-BOND 201 is an excellent electrical insulator, and provides superior resistance to vapors and gases, water, galvanic action, petroleum fuels, salt solutions, and many other organic and inorganic compounds. AA-BOND 201 develops significant properties 1 hour after mixing. However, an extended cure of 4-6 hours at 25°C is required for fully matured bonds. Note: AA-BOND 201 develops a high exotherm. Use immediately after mixing. The exothermic reaction begins within 2 minutes after initiating the mixing step, so have everything ready before mixing. GENERAL PROPERTIES Appearance Slight haze/ slight straw Cure Type Room temperature or Heat cure Benefits Resistant to many organic/inorganics Strong bond strength Great electrical insulator Durable Mix Ratio by weight 100:100 / Resin:Hardener Substrates metals, plastics, concrete, sheetrock, tile, marble, stone, rock, plaster, cement, glass fabrics, wood, leather and rigid plastics Operating Temperature -60 to 110 °C Typical Application(s) Anything requiring the unique properties this adhesive offers Pot Life 5 minutes UNCURED PROPERTIES Viscosity @ 25 °C, mPa·s (cP) Thixotropic Solids Content 100% Specific Gravity, mixed 1.2 g/cc CURE SCHEDULE 30 minutes @ 65°C 2 hours @ 25°C MISC PROPERTIES Volume Resistivity 5.00e+11 ohm-cm Dielectric Constant 4.8 Dielectric Strength 410kV/in CTE, linear 33.3 µin/in-°F @ RT Hardness, Shore D 70 Glass Transition Temp, Tg 25.0 °C, 77.0 °F GENERAL INFORMATION For safe handling information on this product, consult the Material Safety Data Sheet, (MSDS). HOW TO USE Carefully clean and dry all surfaces to be bonded. Apply AA-BOND 201 completely mixed adhesive to the prepared surfaces, and gently press these surfaces together. Contact pressure is adequate for strong, reliable bonds; however, maintain contact until adhesive is completely cured. Some separation of components is common during shipping and storage. For this reason, it is recommended that the contents of the shipping container be thoroughly mixed prior to use. Some ingredients in this formulation provided may crystallize when subjected to low temperature storage. A gentle warming cycle of 52°C for 30 minutes prior to mixing components may be necessary. Crystallized epoxy components do not react as well as liquid components and should be re-dissolved prior to use for best results. AVAILABILITY This epoxy can be supplied in various different packages.

• Industrial Grade Epoxy / Odorless
• Mechanical Properties Hardness, Shore D 70 Cure schedule 2 hours at 25°C at 30min at 65°C
• Adheres to 99% of Substrates.
• High Heat Tolerance
• Good to use outdoors.