Belzona 1811 Ceramic Carbide 2kg Kit Epoxy Based Repair Composite for Pipe Valve Abrasion Resistant Metal Protection Room Temperature Cure Strong Bonding Solvent Free Base 1.788kg Solidifier 0.212kg

Belzona 1811 Ceramic Carbide 2kg one Kit Base A 1.788kg + Solidifier B 0.212kg = 2kg Mixed A 2-part epoxy-based composite material incorporating abrasion resistant ceramic aggregates for the repair and protection of metal surfaces suffering from sliding abrasion. Resist deformation damage and wear providing long-term abrasion resistance. This highly durable composite material can be applied without the need for specialist tools to unlimited thickness onto vertical and horizontal surfaces up to a dry temperature of 80°C (176°F). Will not corrode and is resistant to a wide range of chemicals. It will bond to a variety of substrates providing a seamless lining coupled with excellent abrasion and wear resistance to coarse materials. Key benefits: High abrasion and wear resistance Will not corrode Solvent-free allowing it to be applied safely in confined areas Excellent bonding to many metal surfaces including steel and cast iron Application and cure at room temperature - no hot work involved Long working life Fast cure rate ensures prompt return to service High mechanical strength Applications: Protection of pipework, pipe bends, elbows and valves from abrasion Bonding and grouting tiles and wear plates where high abrasion resistance is required Repair of screw conveyors, centrifuges and pump impellers damaged by erosion and corrosion Linings for worn hoppers, chutes, mixer blades and other equipment subject to abrasion Working Life 41°F(5°C): 3 hrs; 50°F(10°C): 120 min; 68°F(20°C): 60 min. Base Color: Black. Solidifier Color: Red. Mixing Ratio (Base : Solidifier) by Weight: 8.5 : 1; by Volume: 4 : 1. Mixed Density: 2.18 g/cm³. Slump Resistance: Nil at 0.5 inch (12.7 mm). VOC Content: 0.08% / 1.79 g/L.

• Belzona 1811 Ceramic Carbide, 2kg one Kit. Base A 1.788kg + Solidifier B 0.212kg = 2kg. A 2-part epoxy-based composite material incorporating abrasion resistant ceramic aggregates for the repair and protection of metal surfaces suffering from sliding abrasion. Resist deformation damage and wear providing long-term abrasion resistance.
• Working Life 41°F(5°C): 3 hrs; 50°F(10°C): 120 min; 68°F(20°C): 60 min. Base Color: Black. Solidifier Color: Red. Mixing Ratio (Base : Solidifier) by Weight: 8.5 : 1; by Volume: 4 : 1. Mixed Density: 2.18 g/cm³. Slump Resistance: Nil at 0.5 inch (12.7 mm). VOC Content: 0.08% / 1.79 g/L.
• Protects pipes, bends, elbows, valves from abrasion. Bonds and grouts tiles, wear plates with high abrasion resistance. Repairs screw conveyors, centrifuges, pump impellers damaged by erosion. Linings for worn hoppers, chutes, mixer blades, abrasion-prone equipment.
• High abrasion and wear resistance. Corrosion-resistant. Solvent-free, safe for confined areas. Excellent bonding to metals like steel, cast iron. Room temperature application, no hot work. Long working life. Fast cure for quick service return. High mechanical strength.
• Curing Time (0.25 in. / 6mm) Involving No Loading: 24 hrs/5°C (41°F), 16 hrs/10°C (50°F), 12 hrs/15°C (59°F), 8 hrs/20°C (68°F), 6 hrs/25°C (77°F), 3 hrs/30°C (86°F); Machining / Light Loading: 36 hrs/5°C (41°F), 24 hrs/10°C (50°F), 18 hrs/15°C (59°F), 12 hrs/20°C (68°F), 8 hrs/25°C (77°F), 4 hrs/30°C (86°F); Full Mechanical Thermal Loading: 7 days/5°C (41°F), 5 days/10°C (50°F), 4 days/15°C (59°F), 3 days/20°C (68°F), 2 days/25°C (77°F), 1.5 days/30°C (86°F)